Common type of heat exchanger corrosion of metal
Publisher:admin  Time:2013-12-25 15:30:38  Click:1181

Corrosion is the destruction of the surrounding medium under the action of a chemical or electrochemical , and often the joint action and physical , mechanical or biological factors of metal produced , that under the action of the metal produced by the environment in which it destruction.

Plate heat exchanger common types of corrosion of metal in the following categories :

Uniform corrosion over the entire exposed surface of the medium , or generated in a larger area , the macro is called homogeneous uniform corrosion corrosion damage .

Crevice corrosion of the metal surface and the gap is covered by the site will produce severe crevice corrosion .

Two different contact corrosion potential of the metal or alloy in contact with each other and immersed in the electrolyte is dissolved in the precursor solution , it is the current passing between them, the positive potential of the metal corrosion rate decreased with increasing the negative potential of the metal corrosion rate .

Erosion-corrosion erosion-corrosion due to the relative motion between the dielectric and metal surfaces leaving a corrosion process accelerated corrosion .

Selective etching of an element in the alloy due to corrosion , a phenomenon known as preferential access to selective etching medium .

Pitting focused on metal surfaces greater depth of individual dots called pitting corrosion , also known as holes , pitting .

Intergranular corrosion Intergranular corrosion is the area near the grain boundary and the grain boundary corrosion of the metal or alloy of priority , and the grain itself is a relatively small etching corrosion.

Hydrogen damage to the metal in an electrolyte solution , due to corrosion , pickling, cathodic protection or plating can produce damage caused by hydrogen permeation .

Stress corrosion cracking (SCC) and corrosion fatigue is within a certain system of metal- dielectric materials due to the combined effect of corrosion and tensile stress caused by the fracture.

Pre:Plate heat exchanger used in chemical industry
Next:Low-carbon technological innovation will become the future direction of environmental heat
    
 
Home | About us | News | Product | Honor | Feedback | Contact
Copyrightv(c) Wuxi Zhongbo heat exchanger Co.,Ltd All reserved.
Address:Wuxi City, Jiangsu Province town of Leaf Bridge Hudai Tel:+86-510-85589898 85586021 85586011 Fax:+86-510-85589798
E-mail:sales@zhbo.com.cn Http://www.zhbo.com.cn
Links:Doors prices  Winch drum  Power Transformers  Stainless steel sheet  Wood flooring
Is the record
Technical support   Ltall